TPR,博罗TPR厂家,TPR耳机线料 tpr材料 TPR产品
TPS弹性体的主要加工成型方法
TPS类弹性体极易加工成型,常规的加工方法如注塑(包括单物料注塑成型及双物料/多物料注塑成型),挤出,压延(淋膜),吹塑等都可以成型,TPE 弹性体还可以熔胶成液体态,再浇注入预定的模具中,成型冷却即可。
TPE/TPR与PVC之区别比较
TPE/TPR与PVC软胶基本组成:TPE/TPR软胶,是以硬质SEBS/SBS (聚苯乙烯--丁二烯--苯乙烯嵌段共聚物)为主要基材,添加软化油,填充物及其他成分制成的功能性复合材料。
PVC软胶是以聚氯乙烯为主要基材,添加软化剂(增塑剂),抗稳定剂等其他组分,制成的具有橡胶弹性的复合软胶材料。
产品说明Product description |
||||||||
· RN80B-02是一款以SEBS为主基材的高分子材料,耐磨性好,成型快速。 · RN80B-02 is a kind of polymer material with SEBS as major base material which has good wear resistance.Also it can be taken shape rapidly. |
||||||||
关键特性Key characteristic |
||||||||
1.表面哑,手感舒适干爽。dumb surface,dry and comfortable touch 2.可粘接PP,强度非常高very high bonding strength, adhesive material:PP 3.成型快、不粘模具。rapid molding,non-stick mold 4.表面耐刮擦,不易起毛屑。scratch resistance on the surface,not easy to fluff |
||||||||
功能Function |
||||||||
产品应用 Main application |
1 汽车用品Automotive products |
3手把Handlebar |
||||||
2 运动器材Sports equipment |
4玩具产品Toy products |
|||||||
加工方法Processing method |
注塑成型Injection molding |
|||||||
环保认证 Environmental certification |
ROHS |
REACH |
EN71-3 |
|||||
PAHS |
ASTM-F963 |
Phthalate |
||||||
颜色Color |
本色 Natural |
|||||||
气味Smell |
少许树脂味A little resin smell |
|||||||
外型Appearance |
圆球形小颗粒Cylindrical particle,about 3mm×1.5mm |
|||||||
储藏期Storage period |
常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months |
|||||||
包装方式Packaging method |
25公斤/袋 25kg/bag |
|||||||
物理性能Physical properties |
结果Result |
单位Unit |
方法Method |
成型条件Molding condition |
||||
比重Specific gravity |
1.04±0.02 |
g/cm3 |
ASTM D792 |
干燥温度Drying temp 80℃ |
||||
硬度Hardness |
80±5 |
shoreA |
ASTM D2240 |
干燥时间Drying time 2Hours |
||||
拉伸强度Tensile strength |
>6 |
Mpa |
ASTM D412 |
射嘴温度Nozzle temp 190℃ |
||||
断裂延伸Elongation at break |
<450 |
% |
ASTM D412 |
螺筒一段温度Screw 1 temp 180℃ |
||||
撕裂强度Tearing strength |
>35 |
Kn/m |
ASTM D624 |
螺筒二段温度Screw 2 temp 170℃ |
||||
熔融指数Melt index |
>10 |
g/10min |
ASTM D1238 |
螺筒三段温度Screw 3 temp 160℃ |
||||
注意事项Matters need attention |
||||||||
清洗料管 Purge compound |
需使用PP或 PE清洗干净机台螺杆,且把机台射嘴彻底清除干净please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean |
|||||||
着色 Coloring
|
请选择以PE或EVA为基材之色母,切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压,才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion |
|||||||
回收 Recycling |
二次料(水口料)回收比率建议最多20%。 Consistent regrind usage of up to 20% is permissible |