PP油性母粒S0511 油性测试专用母粒

  • 产品描述

  • 技术资料表

    Technical Data Sheet(TDS)

    产品信息 Product information

    品牌

    Brand

    易来极

    ELE KEY

    材料类型

    Material Type

    PP油性母粒

    PP Oiliness Masterbatch

    牌号

    Geade

    S0511

    特性 Characteristic

    ·亲油配方，提高油性颗粒物Lipophilic formula to improve oily particles
     

    ·分散性能极佳Excellent dispersion
     

    ·稳定出丝Stable filament
     

    ·增大调机工艺参数窗口Increase the window of adjusting process parameters

    外观 Appearance

    ·圆柱状 3.5-8mm    Cylindrical shape

    颜色 Colour

    ·本白色            Natural

    气味 Smell

    ·接近无味          Almost tasteless

    包装Packing

    ·25KG/包           KG/ package

    用途Applications

    ·熔喷无纺布        Melt Blown Monwoven
     

    ·与绝大多数的熔喷聚丙烯相熔性良好，直接添加，提高油性颗粒物过滤量，改善发硬变脆现象It has good fusibility with the majority of melt blown polypropylene and can be directly added to improve the filtration amount of oily particles and improve the hardening and embrittlement

    通用性能 General Properties

    序号

    No.

    性能

    Properties

    测试值

    Value

    单位

    Unit

    检验方法

    Method

    测试条件

    Test conditon

    1

    熔体流动速率Melt Flow Index

    200±100

    g/10min

    GB/T 3682

    230℃，2.16kg

    2

    熔点Melting Point

    160

    ℃

    GB/T 19466

    10℃/min

    3

    含水量Water content

    < 0.03

    %

    GB/T 6283-2008

    23℃  75%

    4

    密度density

    0.90

    g/cm3

    GB/T 4472-2011

    23℃  75%

    5

    建议添加量Recommended addition   10-20%

     

     

    备注

    Remarks

     

    塑伯S0511油性颗粒物过滤量提升母粒是针对大部分客户对于油性颗粒物过滤量要求（FFP2标准）推出的新产品。采用亲油性的配方工艺，均匀分散于PP（聚丙烯）载体中，成丝后对油性颗粒物具有同性相吸效应，对过滤量的提升与添加量成正比例（建议添加20%以下），随着添加比例增加，熔体流动性降低，故成型温度应同步提高。

    SPP S0511 oil particle filter quantity promotion masterbatch is a new product launched for most customers' requirements for oil particle filter quantity (FFP2 standard).The formulation process with lipophilic property is adopted, which is evenly dispersed in PP (polypropylene) carrier. After being spun, it has the same phase absorption effect on oily particles. The increase of filtration amount is in positive proportion to the addition amount (it is suggested to add less than 20%). With the increase of the addition proportion, the melt fluidity decreases, so the molding temperature should be increased synchronously.

     

    以上数据为我公司测量之理论数据仅供参考，版权所有@广东塑伯新材料有限公司

    The above data for the theory of the measurement data of our company, for your reference only. Copyright @ SPP New

     