TPV、常平TPV供应厂家(在线咨询)、TPV食品级 TPV材料

·EN45A-HL是一款以SEBS为主基材的高性能弹性体，易加工，耐黄变，耐化学溶剂性能非常出色。 ·EN45A-HL is a kind of high performance thermoplastic elastomer based on SEBS as main material.Aslo it has excellent yellowing resistance and chemical solvent resistance properties.It is easy processing.

产品描述

倍韧/BESTPERNE® EN45A-HL

热塑性弹性体Thermoplastic Elastomer

产品说明Product description
·EN45A-HL是一款以SEBS为主基材的高性能弹性体，易加工，耐黄变，耐化学溶剂性能非常出色。 ·EN45A-HL is a kind of high performance thermoplastic elastomer based on SEBS as main material.Aslo it has excellent yellowing resistance and chemical solvent resistance properties.It is easy processing.
关键特性Key characteristic
1.表面哑，手感细腻柔软。Dumb surface, exquisite and soft touch 2.可粘接PP,强度非常高。Very high bonding strength, adhesive material：PP 3.成型快、不粘模具。Rapid molding,non-stick mold
功能Function
产品应用 Main application		1 汽车用品 Automotive products				3手把Handlebar
		2 运动器材Sports equipment				4玩具产品Toy products
加工方法Processing method		注塑成型Injection molding
环保认证 Environmental certification		ROHS		REACH				EN71-3
		PAHS		ASTM-F963				Phthalate
颜色Color		本色 Natural
气味Smell		少许树脂味A little resin smell
外型Appearance		圆球形小颗粒Cylindrical particle，about 3mm×1.5mm
储藏期Storage period		常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months
包装方式Packaging method		25公斤/袋 25kg/bag
物理性能Physical properties		结果Result	单位Unit		方法Method		成型条件Molding condition
比重Specific gravity		1.03±0.02	g/cm3		ASTM D792		干燥温度Drying temp 70℃
硬度Hardness		45±5	shoreA		ASTM D2240		干燥时间Drying time 2Hours
拉伸强度Tensile strength		>2	Mpa		ASTM D412		射嘴温度Nozzle temp 190℃
断裂延伸Elongation at break		>400	%		ASTM D412		螺筒一段温度Screw 1 temp 190℃
撕裂强度Tearing strength		>14	Kn/m		ASTM D624		螺筒二段温度Screw 2 temp 180℃
熔融指数Melt index		>1	g/10min		ASTM D1238		螺筒三段温度Screw 3 temp 180℃
注意事项Matters need attention
清洗料管 Purge compound	需使用PP或 PE清洗干净机台螺杆，且把机台射嘴彻底清除干净Please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean

为节省材料，将胶头量减至最低，现作出以下工作程序及洗机守则。

　　一. 啤够数、转模前、停机前务必关料斗，把炮筒内的TPE料啤完，直啤到螺杆不能回料为止

　　二. 换TPE料时务必将料桶的材料挖干净。

　　三. 啤黑色或深灰色材料射空胶时要把胶压小、压薄，可用的放在水口一起循环再用。

　　四. 水口、次品与不能循环再用的胶头务必分开装。

　　五. 保持机位卫生干净，尽量不让水口及次品掉到机底、地面、混杂、受污染。

　　六. 开啤前将模面油污、防锈油抹干净，避免次品受污导致不能循环再用。

　　七. 洗机前先将料斗内余料尘粉清理干净，再用洗机料清洗螺杆炮筒，有必要时加入螺杆清洗剂或洗衣粉。清洗将近完成前续渐调低炮筒温度避免炮筒螺杆内的料再度烧焦及熔化成液体引至开啤时不能回料。

　　八. 可以使用白色及透明PP来进行清洗。

　　十. 一般情况下啤白色后转啤灰色、黑色均不用洗机。

　　十一. 啤TPE时停机不超过15分钟，再啤时不用射空胶。试啤时将啤机熔胶量调至大约成品用胶量,射空胶三次即可开啤。