东莞TPR_广东TPR_广东TPR原料供应商 TPR材料

·TN85A-01是一款高性能高分子材料，与尼龙的粘接强度高。材料耐高温。不粘模具，可快速成型。 ·TN85A-01 is a high performance polymer material, and the high bonding strength of nylon. Material resistance to high temperature. Non stick mold, can be rapid prototyping.

产品描述

倍韧/BESTPERNE® TN85A-01

熱塑性彈性體Thermoplastic Elastomer

產品說明Product description
·TN85A-01是一款高性能高分子材料，与尼龙的粘接强度高。材料耐高温。不粘模具，可快速成型。 ·TN85A-01 is a high performance polymer material, and the high bonding strength of nylon. Material resistance to high temperature. Non stick mold, can be rapid prototyping.
關鍵特性Key characteristic
表面哑，手感细腻柔软。dumb surface, exquisite and soft feeling 可以包PA It can be spliced with PA 成型快、不粘模具。rapid molding,non-stick mold 表面耐刮擦，不易起毛屑。scratch resistance on the surface,not easy to fluff
功能Function
产品应用 main application	工具手把Tool hand				汽车产品Automotive products
	仪器外壳Instrument housing
加工方法Processing method	注塑成型Injection molding
环保认证 Environmental certification	ROHS		REACH				EN71-3
	PAHS		ASTM-F963				Phthalate
颜色Color	本色 Natural
气味Smell	少许树脂味A little resin smell
外型Appearance	圆球形小颗粒Cylindrical particle，about 3mm×1.5mm
储藏期Storage period	常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months
包装方式Packaging method	25公斤/袋 25kg/bag
物理性能Physical properties	结果Result	单位Unit		方法Method		成型条件Molding condition
比重Specific gravity	1.05±0.02	g/cm3		ASTM D792		干燥温度Drying temp 70℃
硬度Hardness	85±5	shoreA		ASTM D2240		干燥时间Drying time 2Hours
拉伸强度Tensile strength	4±1	Mpa		ASTM D412		射嘴温度Nozzle temp 220℃
断裂延伸Elongation at break	200±50	%		ASTM D412		螺筒一段温度Screw 1 temp 210℃
撕裂强度Tearing strength	20±3	Kn/m		ASTM D624		螺筒二段温度Screw 2 temp 200℃
熔融指数Melt index	5±3	g/10min		ASTM D1238		螺筒三段温度Screw 3 temp 190℃

时间

　　完成一次注射过程所需的时间称为成型周期。成型周期包括充模时间、保压时间、冷却时间和其他时间（开模、脱模、闭模等），直接影响劳动生产率和设备利用率。TPU的成型周期通常决定于硬度、制件厚度和构型，TPU硬度高周期短，塑件厚周期长，塑件构型复杂周期长，成型周期还与模具温度有关。TPU成型周期一般在20~60s之间。

　　注射速度

　　注射速度主要决定于TPU制品的构型。端面厚的制品需要较低的注射速度，端面薄则注射速度较快。

　　螺杆转速

　　加工TPU制品通常需要低剪切速率，因而以较低的螺杆转速为宜。TPU的螺杆转速一般为20~80r/min，则优选20~40r/min。

关键词: