东莞TPEE原料 -DG55 厂家大量供应tpEE包胶尼龙
倍韧/BESTPERNE® TE95A-02
热塑性弹性体Thermoplastic Elastomer
|
产品说明Product description |
||||||||
|
·TE95A-02是一款高性能材料，具有非常好的弹性，强度，成型性快。 ·TE95A-02 is a kind of high performance material which has very excellent elasticity and strength.Also it can be taken shape rapidly |
||||||||
|
关键特性Key characteristic |
||||||||
|
||||||||
|
功能Function |
||||||||
|
产品应用 Main application |
垫圈Washer |
眼镜框Spectacle frames |
||||||
|
仪器外壳Instrument shell |
|
|||||||
|
加工方法Processing method |
注塑成型Injection molding |
|||||||
|
环保认证 Environmental certification |
ROHS |
REACH |
EN71-3 |
|||||
|
PAHS |
ASTM-F963 |
Phthalate |
||||||
|
颜色Color |
本色 Natural |
|||||||
|
气味Smell |
少许树脂味A little resin smell |
|||||||
|
外型Appearance |
圆球形小颗粒Cylindrical particle，about 3mm×1.5mm |
|||||||
|
储藏期Storage period |
常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months |
|||||||
|
包装方式Packaging method |
25公斤/袋 25kg/bag |
|||||||
|
物理性能Physical properties |
结果Result |
单位Unit |
方法Method |
成型条件Molding condition |
||||
|
比重Specific gravity |
0.9±0.02 |
g/cm3 |
ASTM D792 |
干燥温度Drying temp 70℃ |
||||
|
硬度Hardness |
50±3 |
shoreD |
ASTM D2240 |
干燥时间Drying time 3Hours |
||||
|
拉伸强度Tensile strength |
14±2 |
Mpa |
ASTM D412 |
射嘴温度Nozzle temp 190℃ |
||||
|
断裂延伸Elongation at break |
450±100 |
% |
ASTM D412 |
螺筒一段温度Screw 1 temp 180℃ |
||||
|
撕裂强度Tearing strength |
120±8 |
Kn/m |
ASTM D624 |
螺筒二段温度Screw 2 temp 170℃ |
||||
|
熔融指数Melt index |
6±2 |
g/10min |
ASTM D1238 |
螺筒三段温度Screw 3 temp 160℃ |
||||
|
注意事项Matters need attention |
||||||||
|
清洗料管 Purge compound |
需使用PP或 PE清洗干净机台螺杆，且把机台射嘴彻底清除干净please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean |
|||||||
|
着色 Coloring
|
请选择以PE或EVA为基材之色母，切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压，才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion |
|||||||
|
回收 Recycling |
二次料（水口料）回收比率建议最多5%。 Consistent regrind usage of up to 5% is permissible |
|||||||
以上数据为我公司测量之理论数据仅供参考，版权所有@惠州塑伯新材料有限公司The above data for the theory of the measurement data of our company, for your reference only. Copyright @ Huizhou SPP New Material Co., Ltd.
时间
完成一次注射过程所需的时间称为成型周期。成型周期包括充模时间、保压时间、冷却时间和其他时间（开模、脱模、闭模等），直接影响劳动生产率和设备利用率。TPU的成型周期通常决定于硬度、制件厚度和构型，TPU硬度高周期短，塑件厚周期长，塑件构型复杂周期长，成型周期还与模具温度有关。TPU成型周期一般在20~60s之间。
注射速度
注射速度主要决定于TPU制品的构型。端面厚的制品需要较低的注射速度，端面薄则注射速度较快。
螺杆转速
加工TPU制品通常需要低剪切速率，因而以较低的螺杆转速为宜。TPU的螺杆转速一般为20~80r/min，则优选20~40r/min。