东莞TPEE原料 -DG55 厂家大量供应tpEE包胶尼龙

·TE95A-02是一款高性能材料，具有非常好的弹性，强度，成型性快。 ·TE95A-02 is a kind of high performance material which has very excellent elasticity and strength.Also it can be taken shape rapidly

产品描述

倍韧/BESTPERNE® TE95A-02

热塑性弹性体Thermoplastic Elastomer

产品说明Product description
·TE95A-02是一款高性能材料，具有非常好的弹性，强度，成型性快。 ·TE95A-02 is a kind of high performance material which has very excellent elasticity and strength.Also it can be taken shape rapidly
关键特性Key characteristic
高强度，高弹性high strength，high elasticity 耐黄变，耐候性，耐油污，耐化学溶剂性优秀.good yellowing resistance，weather resistance，oil resistance，and chemical solvent resistance 成型快、不粘模具。rapid molding，non-stick mold
功能Function
产品应用 Main application		垫圈Washer				眼镜框Spectacle frames
		仪器外壳Instrument shell
加工方法Processing method		注塑成型Injection molding
环保认证 Environmental certification		ROHS		REACH				EN71-3
		PAHS		ASTM-F963				Phthalate
颜色Color		本色 Natural
气味Smell		少许树脂味A little resin smell
外型Appearance		圆球形小颗粒Cylindrical particle，about 3mm×1.5mm
储藏期Storage period		常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months
包装方式Packaging method		25公斤/袋 25kg/bag
物理性能Physical properties		结果Result	单位Unit		方法Method		成型条件Molding condition
比重Specific gravity		0.9±0.02	g/cm3		ASTM D792		干燥温度Drying temp 70℃
硬度Hardness		50±3	shoreD		ASTM D2240		干燥时间Drying time 3Hours
拉伸强度Tensile strength		14±2	Mpa		ASTM D412		射嘴温度Nozzle temp 190℃
断裂延伸Elongation at break		450±100	%		ASTM D412		螺筒一段温度Screw 1 temp 180℃
撕裂强度Tearing strength		120±8	Kn/m		ASTM D624		螺筒二段温度Screw 2 temp 170℃
熔融指数Melt index		6±2	g/10min		ASTM D1238		螺筒三段温度Screw 3 temp 160℃
注意事项Matters need attention
清洗料管 Purge compound	需使用PP或 PE清洗干净机台螺杆，且把机台射嘴彻底清除干净please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean
着色 Coloring	请选择以PE或EVA为基材之色母，切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压，才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion
回收 Recycling	二次料（水口料）回收比率建议最多5%。 Consistent regrind usage of up to 5% is permissible

时间

　　完成一次注射过程所需的时间称为成型周期。成型周期包括充模时间、保压时间、冷却时间和其他时间（开模、脱模、闭模等），直接影响劳动生产率和设备利用率。TPU的成型周期通常决定于硬度、制件厚度和构型，TPU硬度高周期短，塑件厚周期长，塑件构型复杂周期长，成型周期还与模具温度有关。TPU成型周期一般在20~60s之间。

　　注射速度

　　注射速度主要决定于TPU制品的构型。端面厚的制品需要较低的注射速度，端面薄则注射速度较快。

　　螺杆转速

　　加工TPU制品通常需要低剪切速率，因而以较低的螺杆转速为宜。TPU的螺杆转速一般为20~80r/min，则优选20~40r/min。

关键词:

astm
the
screw
温度
and
of
temp
resistance
成型