高透明TPEE60度注塑级高弹性胶料 热塑性弹性体tpEE

倍韧/BESTPERNE® ZF85AP 热塑性弹性体Thermoplastic Elastomer 产品说明Product description ZF85AP是一款减震高分子材料，耐候性，耐油，耐化学性能优。减震率可达15%，可注塑成型。 ZF85AP- is a shock-absorbing polymer materials, durability, oil resistance, high chemical resistance. Shock absorption rate of up to 15% can be injection molded. 关键特性Key characteristic 1.表面微亮，手感细腻柔软爽滑.              a little bright on the surface，exquisite，smooth and soft touch feeling. 2.超耐磨高强度,高回复性,抗变形excellent wear resistance and deformation resistance，high strength and resilience. 3.成型快、不粘模具.rapid molding，non-stick mold.  4.阻尼效果优异.    Damping effect is good. 功能Function 产品应用 Main application 手机保护套Phone protective cover 仪器外壳Instrument shell 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 注塑、挤出成型Injection and extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle，about 3mm×1.5mm 储藏期Storage period 常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.1±0.02 g/cm3 ASTM D792 干燥温度Drying temp     60 ℃ 硬度Hardness 85±3 shoreA ASTM D2240 干燥时间Drying time      2h 拉伸强度Tensile strength >5 Mpa ASTM D412 射嘴温度Nozzle temp     200℃ 断裂延伸Elongation at break >350 % ASTM D412 螺筒一段温度Screw 1 temp 190℃ 撕裂强度Tearing strength >45 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 180℃ 熔融指数Melt index >10 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 170℃
  • 产品描述

  • 倍韧/BESTPERNE® ZF85AP

    热塑性弹性体Thermoplastic Elastomer

    产品说明Product description

    ZF85AP是一款减震高分子材料，耐候性，耐油，耐化学性能优。减震率可达15%，可注塑成型。

    ZF85AP- is a shock-absorbing polymer materials, durability, oil resistance, high chemical resistance. Shock absorption rate of up to 15% can be injection molded.

    关键特性Key characteristic

    1.表面微亮，手感细腻柔软爽滑.              a little bright on the surface，exquisite，smooth and soft touch feeling.

    2.超耐磨高强度,高回复性,抗变形excellent wear resistance and deformation resistance，high strength and resilience.

    3.成型快、不粘模具.rapid molding，non-stick mold. 

    4.阻尼效果优异.    Damping effect is good.

    功能Function

    产品应用

    Main application

    手机保护套Phone protective cover

    仪器外壳Instrument shell

    电子器件粘胶配件Electronic plastic accessories

    加工方法Processing method

    注塑、挤出成型Injection and extrusion molding

    环保认证

    Environmental certification

    ROHS

    REACH

    EN71-3

    PAHS

    ASTM-F963

    Phthalate

    颜色Color

    本色Natural

    气味Smell

    少许树脂味A little resin smell

    外型Appearance

    圆球形小颗粒Cylindrical particle，about 3mm×1.5mm

    储藏期Storage period

    常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months

    包装方式Packaging method

    25公斤/袋 25kg/bag

    物理性能Physical properties

    结果Result

    单位Unit

    方法Method

    成型条件Molding condition

    比重Specific gravity

    1.1±0.02

    g/cm3

    ASTM D792

    干燥温度Drying temp     60 ℃

    硬度Hardness

    85±3

    shoreA

    ASTM D2240

    干燥时间Drying time      2h

    拉伸强度Tensile strength

    >5

    Mpa

    ASTM D412

    射嘴温度Nozzle temp     200℃

    断裂延伸Elongation at break

    >350

    %

    ASTM D412

    螺筒一段温度Screw 1 temp 190℃

    撕裂强度Tearing strength

    >45

    Kn/m

    ASTM D624

    螺筒二段温度Screw 2 temp 180℃

    熔融指数Melt index

    >10

    g/10min

    ASTM D1238

    螺筒三段温度Screw 3 temp 170℃

    塑料增韧的影响因素

    　　塑料增韧的影响因素可以从基体的特性、弹性体相的结构和含量及两相间的粘合力等三个方面考虑。

    　　1.树脂基体特性的影响

    　　树脂基体特性对韧性的影响主要有两方面：

    　　一是树脂分子量及其分布的影响，增加分子量可提高冲击强度，而增加低分子量组分会降低冲击强度。当然，分子量过高加工性能下降，反而不利于制品的综合性能。

    　　二是基体组成及其特性的影响，一般来说，在其他条件相同的条件下，基体分子链柔性越大，延展性越大，基体树脂越容易增韧。

    　　2.弹性体的影响

    　　作为分散相，弹性体的含量、粒径、粒子间距、Tg、交联度等方面对塑料韧性均有影响。

    　　3.弹性体相与基体树脂之间粘合力的影响

    　　只有在弹性体相与基体之间有良好的粘合力时，弹性体粒子才能有效引发、终止银纹并分担施加的负荷。粘合力弱则不能很好地发挥以上三种功能，冲击强度就低。为增加两相之间的粘合力，可采用接枝或者共聚的方法，所生成的共聚物起着增容剂的作用，从而大大提高冲击强度。

     