发泡级TPEE 厂家直接供应指压板TPEE原料 塑胶原料

倍韧/BESTPERNE® ZF65AP-1 热塑性弹性体Thermoplastic Elastomer 产品说明Product description ZF65AP-1是一款减震高分子材料，耐候性，耐油，耐化学性能优。减震率可达15%，可注塑成型。 ZF65AP-1 is a shock-absorbing polymer materials, durability, oil resistance, high chemical resistance. Shock absorption rate of up to 15% can be injection molded. 关键特性Key characteristic 1.表面微亮，手感细腻柔软爽滑.              a little bright on the surface，exquisite，smooth and soft touch feeling. 2.超耐磨高强度,高回复性,抗变形excellent wear resistance and deformation resistance，high strength and resilience. 3.成型快、不粘模具.rapid molding，non-stick mold.  4.阻尼效果优异.    Damping effect is good. 功能Function 产品应用 Main application 手机保护套Phone protective cover 仪器外壳Instrument shell 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 注塑、挤出成型Injection and extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle，about 3mm×1.5mm 储藏期Storage period 常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.13±0.02 g/cm3 ASTM D792 干燥温度Drying temp     60 ℃ 硬度Hardness 65±5 shoreA ASTM D2240 干燥时间Drying time      2h 拉伸强度Tensile strength >4 Mpa ASTM D412 射嘴温度Nozzle temp     200℃ 断裂延伸Elongation at break >400 % ASTM D412 螺筒一段温度Screw 1 temp 190℃ 撕裂强度Tearing strength >20 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 180℃ 熔融指数Melt index >1 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 170℃
  • 产品描述

  • 倍韧/BESTPERNE® ZF65AP-1

    热塑性弹性体Thermoplastic Elastomer

    产品说明Product description

    ZF65AP-1是一款减震高分子材料，耐候性，耐油，耐化学性能优。减震率可达15%，可注塑成型。

    ZF65AP-1 is a shock-absorbing polymer materials, durability, oil resistance, high chemical resistance. Shock absorption rate of up to 15% can be injection molded.

    关键特性Key characteristic

    1.表面微亮，手感细腻柔软爽滑.              a little bright on the surface，exquisite，smooth and soft touch feeling.

    2.超耐磨高强度,高回复性,抗变形excellent wear resistance and deformation resistance，high strength and resilience.

    3.成型快、不粘模具.rapid molding，non-stick mold. 

    4.阻尼效果优异.    Damping effect is good.

    功能Function

    产品应用

    Main application

    手机保护套Phone protective cover

    仪器外壳Instrument shell

    电子器件粘胶配件Electronic plastic accessories

    加工方法Processing method

    注塑、挤出成型Injection and extrusion molding

    环保认证

    Environmental certification

    ROHS

    REACH

    EN71-3

    PAHS

    ASTM-F963

    Phthalate

    颜色Color

    本色Natural

    气味Smell

    少许树脂味A little resin smell

    外型Appearance

    圆球形小颗粒Cylindrical particle，about 3mm×1.5mm

    储藏期Storage period

    常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months

    包装方式Packaging method

    25公斤/袋 25kg/bag

    物理性能Physical properties

    结果Result

    单位Unit

    方法Method

    成型条件Molding condition

    比重Specific gravity

    1.13±0.02

    g/cm3

    ASTM D792

    干燥温度Drying temp     60 ℃

    硬度Hardness

    65±5

    shoreA

    ASTM D2240

    干燥时间Drying time      2h

    拉伸强度Tensile strength

    >4

    Mpa

    ASTM D412

    射嘴温度Nozzle temp     200℃

    断裂延伸Elongation at break

    >400

    %

    ASTM D412

    螺筒一段温度Screw 1 temp 190℃

    撕裂强度Tearing strength

    >20

    Kn/m

    ASTM D624

    螺筒二段温度Screw 2 temp 180℃

    熔融指数Melt index

    >1

    g/10min

    ASTM D1238

    螺筒三段温度Screw 3 temp 170℃

    中空成型

    　　中空成型是树脂特有的成型方法，一般的硫化橡胶成型不能应用，而TPV材料可采用这种方法。如汽车用齿条和齿轮护罩，用TPV替代氯丁橡胶，采用中空成型方法可使该部件的成本降低30%一40%，且可轻量化，制品性能也有所改善;用于汽车净化的空气通风管，采用三维交换吹塑成型技术能够一边切断TPV和聚丙烯，一边吹气挤出(管子的两端采用TPV以提高密封性;管子的其他腹部使用完全交联型TPE以改善屈挠疲劳性和柔软性;为降低成本和保持一定的刚性，在管子的直线部位使用PP) [5]。以往由几个工件组合使用的部件可用一个工件代替，可大幅度缩减组合工序。此外，中空成型技术也在以一般吹气挤出为基础进行技术革新，开发成型精度良好的注射吹气成型、模压吹气成型等新技术。

     