高回弹TPEE 新材料 厂家直销TPEE二次注塑包胶

 
产品编号:
ZF55B
倍韧/BESTPERNE® ZF55B 热塑性弹性体Thermoplastic Elastomer 产品说明Product description 一款高性能吸震材料,具有特别舒适的手感。  high performance shock absorption material,with a special and comfortable feel. 关键特性Key characteristic 1.表面微亮,手感细腻柔软爽滑.   A little bright on the surface,exquisite,smooth and soft touch feeling. 2.阻尼效果优异.    Damping effect is good. 功能Function 产品应用 Main application 手机保护套Phone protective cover 密封垫片Sealing gasket 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 注塑、挤出成型Injection and extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle,about 3mm×1.5mm 储藏期Storage period 常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.02±0.02 g/cm3 ASTM D792 干燥温度Drying temp     60 ℃ 硬度Hardness 55±5 shoreA ASTM D2240 干燥时间Drying time      2h 拉伸强度Tensile strength >4 Mpa ASTM D412 射嘴温度Nozzle temp     200℃ 断裂延伸Elongation at break >300 % ASTM D412 螺筒一段温度Screw 1 temp 190℃ 撕裂强度Tearing strength >22 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 180℃ 熔融指数Melt index >3 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 170℃ 压缩永久变形(高温)Compression set (high temperature) 103   % ISO 815 70℃/24h,压缩量为25% 压缩永久变形(常温)Compression set (normal temperature) 57    % ISO 815 23℃/72h,压缩量为25% 脆化温度Embrittlement temperature -30 ℃ ISO 812  
 
产品描述

倍韧/BESTPERNE® ZF55B

热塑性弹性体Thermoplastic Elastomer

产品说明Product description

一款高性能吸震材料,具有特别舒适的手感。

 high performance shock absorption material,with a special and comfortable feel.

关键特性Key characteristic

1.表面微亮,手感细腻柔软爽滑.   A little bright on the surface,exquisite,smooth and soft touch feeling.

2.阻尼效果优异.    Damping effect is good.

功能Function

产品应用

Main application

手机保护套Phone protective cover

密封垫片Sealing gasket

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

注塑、挤出成型Injection and extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

本色Natural

气味Smell

少许树脂味A little resin smell

外型Appearance

圆球形小颗粒Cylindrical particleabout 3mm×1.5mm

储藏期Storage period

常温下通风干燥,24个月Ventilated dry at normal temperatureabout 24 months

包装方式Packaging method

25公斤/25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.02±0.02

g/cm3

ASTM D792

干燥温度Drying temp     60

硬度Hardness

55±5

shoreA

ASTM D2240

干燥时间Drying time      2h

拉伸强度Tensile strength

>4

Mpa

ASTM D412

射嘴温度Nozzle temp     200

断裂延伸Elongation at break

>300

%

ASTM D412

螺筒一段温度Screw 1 temp 190

撕裂强度Tearing strength

>22

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 180

熔融指数Melt index

>3

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 170

压缩永久变形(Compression set (high temperature)

103  

%

ISO 815

70/24h,压缩量为25%

压缩永久变形(常温Compression set (normal temperature)

57   

%

ISO 815

23/72h,压缩量为25%

脆化温度Embrittlement temperature

-30

ISO 812

 

塑料增韧的方法

  塑料增韧的主要方法是以弹性体(TPE)为分散相,塑料为基体共混增韧,能大幅提高塑料的冲击强度。弹性体增韧塑料主要要满足三个条件:

  1.弹性体与树脂形成两相结构,但也要有适度的相容性以保证两相之间有良好的粘接力;

  2.弹性体添加量要达到一定的份数;

  3.弹性体的分子链柔性要较低,也就是说需要较低的Tg,尤其是低温增韧时弹性体的Tg越低,低温韧性越好。

  由于纯弹性体是非极性材料,而塑料(如PA、PBT)是极性材料,二者不相容,纯弹性体不能有效增韧塑料,故而需要通过接枝改性使POE形成POE接枝物,接枝的官能团能够与基材端基反应从而提供一定的相容性,使两相具有很好的粘接性,从而能够使基材树脂大幅提高冲击强度。如CMG5805-L(POE-g-MAH)的MAH可与尼龙的端胺基反应,可以有效增韧PA,当5805-L添加一定份数后,形成了超韧材料.

 

暂时没有内容信息显示
请先在网站后台添加数据记录。
塑伯TPE
搜索
搜索
塑伯橡塑胶
智能穿戴硬件联盟

  Copyright © 2021 广东塑伯新材料有限公司

All Rights Reserved. 粤ICP备2021071326号

销售热线:400-800-0302      手机:13602342196       电话:0752-6768128       传真:0752-6768088

地址:广东省惠州市博罗县石湾镇黄西工业园径二路  邮箱:sales@tpe-sp.com   网址:www.tpe-sp.com