倍韧/BESTPERNE® TA7010 热塑性弹性体Thermoplastic Elastomer 产品说明Product description ·TA7010是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。 ·TA7010 is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly. 关键特性Key characteristic 1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth 2.粘接强度非常高,可粘接材质:ABS.PC TPU。Very high bonding strength, adhesive materials:ABS,PC,TPU. 3.成型快、不粘模具。Rapid molding,non-stick mold 4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff 功能Function 产品应用 Main application 智能手环 Intelligent bracelet   仪器外壳Instrument shell 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 1 注塑成型Injection molding     2 挤出成型Extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色 Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle,about 3mm×1.5mm 储藏期Storage period 常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.15±0.02 g/cm3 ASTM D792 干燥温度Drying temp       90℃ 硬度Hardness 70±5 shoreA ASTM D2240 干燥时间Drying time     2Hours 拉伸强度Tensile strength >9 Mpa ASTM D412 射嘴温度Nozzle temp      190℃ 断裂延伸Elongation at break >600 % ASTM D412 螺筒一段温度Screw 1 temp 180℃ 撕裂强度Tearing strength >40 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 170℃ 熔融指数Melt index >12 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 160℃
 
上一个
下一个
产品描述

倍韧/BESTPERNE® TA7010

热塑性弹性体Thermoplastic Elastomer

产品说明Product description

·TA7010是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。

·TA7010 is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly.

关键特性Key characteristic

1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth

2.粘接强度非常高,可粘接材质:ABS.PC TPUVery high bonding strength, adhesive materialsABS,PC,TPU.

3.成型快、不粘模具。Rapid moldingnon-stick mold

4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff

功能Function

产品应用

Main application

智能手环 Intelligent bracelet

 

仪器外壳Instrument shell

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

1 注塑成型Injection molding     2 挤出成型Extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

本色 Natural

气味Smell

少许树脂味A little resin smell

外型Appearance

圆球形小颗粒Cylindrical particleabout 3mm×1.5mm

储藏期Storage period

常温下通风干燥,24个月Ventilated dry at normal temperatureabout 24 months

包装方式Packaging method

25公斤/25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.15±0.02

g/cm3

ASTM D792

干燥温度Drying temp       90

硬度Hardness

70±5

shoreA

ASTM D2240

干燥时间Drying time     2Hours

拉伸强度Tensile strength

>9

Mpa

ASTM D412

射嘴温度Nozzle temp      190

断裂延伸Elongation at break

>600

%

ASTM D412

螺筒一段温度Screw 1 temp 180

撕裂强度Tearing strength

>40

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 170

熔融指数Melt index

>12

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 160


  (1)避免日光照射TPU。TPU存放区域应阴凉通风,同时TPU可用塑胶袋封包放置在无阳光照射的地方。

  (2)喷施耐黄油漆。油漆的喷施通常有两种形式,一种是模内喷施,一种是模外喷施,耐黄油漆的喷施会在TPU成品表面形成一种保护层,避免TPU表皮与大气接触而污染黄变,这种形式目前已被广泛使用。

  (3)添加抗黄剂。为了加强TPU成品的抗黄能力,往往要在原料中添加一种专用抗黄的抗黄剂,但是抗黄剂价格昂贵,我们在使用抗黄剂时也应衡量其经济效益, 如我们的黑色型体对黄变就不敏感,所以我们可使用较便宜的未添加抗黄剂的非抗黄原料,由于抗黄剂是一种原料添加剂,它添加于A成份中,我们配料时要求搅拌 就是为了分布均匀,达到抗黄效果,否则会出现局部黄变现象。

  (4)使用良好的混合比。良好的比例可以使I液和P液达到最充分的混合反应而不会有未完全反应部分,而有这些现象出现时会使成品抗水解,抗黄能力大大降低,特别是比例中ISO偏多时会加速成品的黄变。

  (5)避免人工操作过程中污染。有较多的TPU成品在整理或挽救的过程中被污染而产生黄变如人体汗液和有机溶剂等,因此TPU制品要特别注意接触体的干净,同时尽可能减少整理程序。
 

 

塑伯TPE
搜索
搜索
塑伯橡塑胶
智能穿戴硬件联盟

  Copyright © 2021 广东塑伯新材料有限公司

All Rights Reserved. 粤ICP备2020127300号

销售热线:400-800-0302      手机:13602342196       电话:0752-6768128       传真:0752-6768088

地址:广东省惠州市博罗县石湾镇黄西工业园径二路  邮箱:sales@tpe-sp.com   网址:www.tpe-sp.com