倍韧/BESTPERNE® TA75C-26 热塑性弹性体Thermoplastic Elastomer 产品说明Product description ·TA75C-26是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。 ·TA75C-26is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly. 关键特性Key characteristic 1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth 2.粘接强度非常高,可粘接材质:ABS.PC TPU。Very high bonding strength, adhesive materials:ABS,PC,TPU. 3.成型快、不粘模具。Rapid molding,non-stick mold 4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff 功能Function 产品应用 Main application 手机保护Phone protective cover 电脑Computer 仪器外壳Instrument shell 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 1 注塑成型Injection molding     2 挤出成型Extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色 Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle,about 3mm×1.5mm 储藏期Storage period 常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.14±0.02 g/cm3 ASTM D792 干燥温度Drying temp       90℃ 硬度Hardness 76±5 shoreA ASTM D2240 干燥时间Drying time     2Hours 拉伸强度Tensile strength >8 Mpa ASTM D412 射嘴温度Nozzle temp      190℃ 断裂延伸Elongation at break >500 % ASTM D412 螺筒一段温度Screw 1 temp 180℃ 撕裂强度Tearing strength >40 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 170℃ 熔融指数Melt index >15 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 160℃
 
产品描述

倍韧/BESTPERNE® TA75C-26

热塑性弹性体Thermoplastic Elastomer

产品说明Product description

·TA75C-26是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。

·TA75C-26is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly.

关键特性Key characteristic

1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth

2.粘接强度非常高,可粘接材质:ABS.PC TPUVery high bonding strength, adhesive materialsABS,PC,TPU.

3.成型快、不粘模具。Rapid moldingnon-stick mold

4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff

功能Function

产品应用

Main application

手机保护Phone protective cover

电脑Computer

仪器外壳Instrument shell

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

1 注塑成型Injection molding     2 挤出成型Extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

本色 Natural

气味Smell

少许树脂味A little resin smell

外型Appearance

圆球形小颗粒Cylindrical particleabout 3mm×1.5mm

储藏期Storage period

常温下通风干燥,24个月Ventilated dry at normal temperatureabout 24 months

包装方式Packaging method

25公斤/25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.14±0.02

g/cm3

ASTM D792

干燥温度Drying temp       90

硬度Hardness

76±5

shoreA

ASTM D2240

干燥时间Drying time     2Hours

拉伸强度Tensile strength

>8

Mpa

ASTM D412

射嘴温度Nozzle temp      190

断裂延伸Elongation at break

>500

%

ASTM D412

螺筒一段温度Screw 1 temp 180

撕裂强度Tearing strength

>40

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 170

熔融指数Melt index

>15

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 160

TPE一般是以SEBS为基材改性而成,TPR一般是以SBS为基材改性而成。

  而SEBS是SBS氢化(所谓氢化是指不饱和分子在特殊的反应条件下,分子中引入氢原子,从而使分子结构达到饱和状态)后的产物。SEBS具有饱和分子结构,其耐老化,耐黄变,耐温,耐腐蚀性能则优于SBS.同样的TPE的相关性能则优于TPR,它们的区别:

  1、TPR颗粒比TPE颗粒更亮面

  2、TPE手感舒适爽滑

  3、TPR则有些粘手

  4、一些需要粘结胶水的制品,如鞋材,工艺品,玩具公仔等,一般用TPR材料,因TPR与胶水粘合比较牢,而用TPE材料与胶水则几乎不粘.另外TPR容易配色,适合做制品色彩鲜艳,表面光亮的产品。TPE与TPR都具有塑料的可塑性及橡胶的弹性,而TPR分子具有类似橡胶的不饱和分子结构,因而更具有橡胶的手感和回弹性。

  5、TPE与TPR燃烧区别:TPE燃烧产生轻烟,而TPR燃烧产生的烟比较浓黑。TPR比TPE难于塑化和加工。

 

塑伯TPE
搜索
搜索
塑伯橡塑胶
智能穿戴硬件联盟

  Copyright © 2021 广东塑伯新材料有限公司

All Rights Reserved. 粤ICP备2021071326号

销售热线:400-800-0302      手机:13602342196       电话:0752-6768128       传真:0752-6768088

地址:广东省惠州市博罗县石湾镇黄西工业园径二路  邮箱:sales@tpe-sp.com   网址:www.tpe-sp.com