TPV、厂家TPV原材料价格鞋底鞋垫、TPV软胶价格 TPV材料

 
产品编号:
TA75C-10
倍韧/BESTPERNE® TA75C-10 热塑性弹性体Thermoplastic Elastomer 产品说明Product description ·TA75C-10是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。 ·TA75C-10 is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly. 关键特性Key characteristic 1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth 2.粘接强度非常高,可粘接材质:ABS.PC TPU。Very high bonding strength, adhesive materials:ABS,PC,TPU. 3.成型快、不粘模具。Rapid molding,non-stick mold 4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff 功能Function 产品应用 Main application 手机保护Phone protective cover 电脑Computer 仪器外壳Instrument shell 电子器件粘胶配件Electronic plastic accessories 加工方法Processing method 1 注塑成型Injection molding     2 挤出成型Extrusion molding 环保认证 Environmental certification ROHS REACH EN71-3 PAHS ASTM-F963 Phthalate 颜色Color 本色 Natural 气味Smell 少许树脂味A little resin smell 外型Appearance 圆球形小颗粒Cylindrical particle,about 3mm×1.5mm 储藏期Storage period 常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months 包装方式Packaging method 25公斤/袋 25kg/bag 物理性能Physical properties 结果Result 单位Unit 方法Method 成型条件Molding condition 比重Specific gravity 1.15±0.02 g/cm3 ASTM D792 干燥温度Drying temp       90℃ 硬度Hardness 75±5 shoreA ASTM D2240 干燥时间Drying time     2Hours 拉伸强度Tensile strength >10 Mpa ASTM D412 射嘴温度Nozzle temp      200℃ 断裂延伸Elongation at break >500 % ASTM D412 螺筒一段温度Screw 1 temp 190℃ 撕裂强度Tearing strength >36 Kn/m ASTM D624 螺筒二段温度Screw 2 temp 180℃ 熔融指数Melt index >8 g/10min ASTM D1238 螺筒三段温度Screw 3 temp 180℃
 
产品描述

倍韧/BESTPERNE® TA75C-10

热塑性弹性体Thermoplastic Elastomer

产品说明Product description

·TA75C-10是一款高性能材料,具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。

·TA75C-10 is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly.

关键特性Key characteristic

1.表面哑,手感细腻爽滑。Dumb surface, the handle is exquisite and smooth

2.粘接强度非常高,可粘接材质:ABS.PC TPUVery high bonding strength, adhesive materialsABS,PC,TPU.

3.成型快、不粘模具。Rapid moldingnon-stick mold

4.表面耐刮擦,不易起毛屑。Scratch resistance on the surface,not easy to fluff

功能Function

产品应用

Main application

手机保护Phone protective cover

电脑Computer

仪器外壳Instrument shell

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

1 注塑成型Injection molding     2 挤出成型Extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

本色 Natural

气味Smell

少许树脂味A little resin smell

外型Appearance

圆球形小颗粒Cylindrical particleabout 3mm×1.5mm

储藏期Storage period

常温下通风干燥,24个月Ventilated dry at normal temperatureabout 24 months

包装方式Packaging method

25公斤/25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.15±0.02

g/cm3

ASTM D792

干燥温度Drying temp       90

硬度Hardness

75±5

shoreA

ASTM D2240

干燥时间Drying time     2Hours

拉伸强度Tensile strength

>10

Mpa

ASTM D412

射嘴温度Nozzle temp      200

断裂延伸Elongation at break

>500

%

ASTM D412

螺筒一段温度Screw 1 temp 190

撕裂强度Tearing strength

>36

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 180

熔融指数Melt index

>8

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 180

TPE材料与哪些材料相似?

  1、PVC的优点:软胶PVC弹性良好;耐老化、耐酸碱性优良;并且PVC成本较为低廉;可快速注塑加工成型。

  PVC的不足:含有毒卤素元素氯,气味大;可能含有毒塑化剂及重金属;燃烧可能释放致癌物质二噁英;低温易变脆,弹性差;存在永久变形。

  2、硅胶的优点:耐高温(200~250℃);手感爽滑;高弹性,永久变形小;无气味,环保无毒;耐老化,耐弱酸碱;较容易通过食品级LFGB橄榄油测试及FDA177.2600正己烷测试。

  硅胶的不足:成型周期较长;材料不能回收再次使用;包覆成型性较差.

  3、橡胶的优点:高耐磨;回弹性,抗撕裂性好;永久变形小;机械性能好;耐高温;耐腐蚀。橡胶的不足:加工工序多,生产周期长;物料不能回收再使用;材料气味大,环保性堪忧;

  4、TPE和TPU都属于软性材料,都具有良好的橡胶弹性.相比较而言,TPE在触感的舒适度方面更为卓越,TPU则更多的呈现优异的弹性和强度.较低硬度的产品(如30A以下),需选用TPE,可以起到防滑缓冲减震回弹的效果.而对于较高硬度(80A以上)的要求弹性好的产品,用TPU才能胜任。
 

 

塑伯TPE
搜索
搜索
塑伯橡塑胶
智能穿戴硬件联盟

  Copyright © 2021 广东塑伯新材料有限公司

All Rights Reserved. 粤ICP备2021071326号

销售热线:400-800-0302      手机:13602342196       电话:0752-6768128       传真:0752-6768088

地址:广东省惠州市博罗县石湾镇黄西工业园径二路  邮箱:sales@tpe-sp.com   网址:www.tpe-sp.com